Immersion ultrasonic testing of surface cracks on thermal barrier coatings
-
摘要: 为有效检测热障涂层(TBCs)表面裂纹,进行了热障涂层表面裂纹水浸超声检测技术的应用研究。以常用的大气等离子喷涂(APS)热障涂层作为试验材料,采用水浸超声检测回波声程差和C扫描图像对不同深度、宽度和长度的热障涂层表面裂纹进行了表征。结果表明:热障涂层基体材料对热障涂层表面裂纹的检测效果无明显影响;通过优化检测参数和合理选用仪器探头,利用水浸超声方法可实现对热障涂层表面深度为0.1 mm、长度为2 mm裂纹的有效检测;水浸超声检测技术可以获得裂纹的长度、深度参数,是解决热障涂层表面裂纹检测问题的有效方法。
-
关键词:
- 热障涂层(TBCs) /
- 表面裂纹 /
- 水浸超声检测 /
- C扫描 /
- 回波声程差
Abstract: In order to effectively detect the surface cracks on thermal barrier coatings (TBCs), the applicability of immersion ultrasonic testing method was studied. The TBCs samples were fabricated by the air plasma spray (APS), which was most commonly used in the TBCs process. The surface cracks with different depth, width and length were characterized by echo path difference and C scan image. Results indicated that the substrate materials had no obvious influence on the immersion ultrasonic testing results. By optimizing the detection parameters and selecting the instruments and probes properly, the surface crack with the depth of 0.1 mm and the length of 2 mm can be detected effectively by the immersion ultrasonic testing method. The length and depth of the surface cracks on TBCs can also be achieved by immersion ultrasonic testing method, make it an effective way to solve the TBCs surface cracks detection problem. -
[1] PADTURE N P,GELL M,JORDAN E H.Thermal barrier coatings for gas-turbine engine applications[J].Science,2002,296(5566):280-284. [2] 郭洪波,宫声凯,徐惠彬.新型高温/超高温热障涂层及制备技术研究进展[J].航空学报,2004,35(10):2722-2732.GUO Hongbo,GONG Shengkai,XU Huibin.Research progress of new high/ultra-high temperature thermal barrier casting and processing technologies[J].Acta Aeronautica et Astronautica Sinica,2014,35(10):2722-2732.(in Chinese) [3] 钟志春.热障涂层表面开裂与界面剥离失效的声发射定量评价[D].湖南 湘潭:湘潭大学,2013.ZHONG Zhichun.Quantitative failure assessment for surface cracking and interface delamination of thermal barrier coatings by acoustic emission[D].Xiangtan Hunan:Xiangtan University,2013.(in Chinese) [4] EVANS A G,MUMM D R,HUTCHINSON J W,et al.Mechanisms controlling the durability of thermal barrier coatings[J].Progress in Materials Science,2011,46(5):505-553. [5] POMEROY M J.Coatings for gas turbine material and long term stability issues[J].Materials and Design,2005,26(3):223-231. [6] MERCER C,FAULHABER S,EVANS A G,et al.A delamination mechanism for thermal barrier coatings subject to calcium-magnesium-alumino-silicate(CMAS) infiltration[J].Acta Materialia,2005,53(4):1029-1039. [7] JIANG Peng,FAN Xueling,SUN Yongle,et al.Competition mechanism of interfacial cracks in thermal barrier coating system[J].Materials and Design,2017,132:559-566. [8] ZHOU Yichun,TONOMORI T,YOSHIDA A,et al.Fracture characteristics of thermal barrier coatings after tensile and bending tests[J].Surface and Coatings Technology,2002,157(2/3):118-127. [9] CHEN Zhubing,WANG Zhongguang,ZHU Shijie.Tensile fracture behavior of thermal barrier coatings on superalloy[J].Surface and Coatings Technology,2011,205(15):3931-3938. [10] QIAN Lihe,ZHU Shijie,KAGAWA Y,et al.Tensile damage evolution behavior in plasma-sprayed thermal barrier coating system[J].Surface and Coatings Technology,2003,173(2/3):178-184. [11] FUKUCHI T,OZEKI T,OKADA M,et al.Nondestructive inspection of thermal barrier coating of gas turbine high temperature components[J].IEEJ Transactions on Electrical and Electronic Engineering,2016,11(4):391-400. [12] FUKUCHI T,FUSE N,FUJII T,et al.Measurement of topcoat thickness of thermal barrier coating for gas turbines using terahertz waves[J].Electrical Engineering in Japan,2013,183(4):1-9. [13] FUKUCHI T,FUSE N,OKADA M,et al.Measurement of refractive index and thickness of topcoat of thermal barrier coating by reflection measurement of terahertz waves[J].Electronics and Communications in Japan,2013,96(12):37-45. [14] FUKUCHI T,FUSE N,OKADA M,et al.Topcoat thickness measurement of thermal barrier coating of gas turbine blade using terahertz wave[J].Electrical Engineering in Japan,2014,189(1):1-8. [15] MA Zhiyuan,ZHAO Yang,LUO Zhongbing,et al.Ultrasonic characterization of thermally grown oxide in thermal barrier coating by reflection coefficient amplitude spectrum[J].Ultrasonics,2014,54(4):1005-1009. [16] ZHAO Yanan,LIN Li,LI Ximeng,et al.Simultaneous determination of the coating thickness and its longitudinal velocity by ultrasonic nondestructive method[J].Ndt & E International,2010,43(7):579-585. [17] TANG Qingju,DAI Jingmin,BU Chiwu,et al.Experimental study on debonding defects detection in thermal barrier coating structure using infrared lock-in thermographic technique[J].Applied Thermal Engineering,2016,107:463-468. [18] LIU Zhanwei,JIAO Dacheng,SHI Wenxiong,et al.Linear laser fast scanning thermography NDT for artificial disbond defects in thermal barrier coatings[J].Optics Express,2017,25:31789-31800. [19] HEEG B,CLARKE D R.Non-destructive thermal barrier coating (TBC) damage assessment using laser-induced luminescence and infrared radiometry[J].Surface and Coatings Technology,2005,200(5/6):1298-1302. [20] 何存富,杨玉娥,杨申,等.毫米波检测热障涂层缺陷的方法研究[J].机械工程学报,2013,49(20):16-21.HE Cunfu,YANG Yu’e,YANG Shen,et al.Feasibility study on defects detection of thermal barrier coatings using millimeter wave[J].Journal of Mechanical Engineering,2013,49(20):16-21.(in Chinese) [21] 郭兴旺,丁蒙蒙.热障涂层厚度及厚度不均热无损检测的数值模拟[J].航空学报,2010,31(1):198-203.GUO Xingwang,DING Mengmeng.Simulation of thermal NDT of thickness and its unevenness of thermal barrier coatings[J].Acta Aeronautica et Astronautica Sinica,2010,31(1):198-203.(in Chinese) [22] YANG Li,ZHONG Zhichun,YOU Jingsong,et al.Acoustic emission evaluation of fracture characteristics in thermal barrier coatings under bending[J].Surface and Coatings Technology,2013,232:710-718. [23] CHEN H L R,ZHANG Binwei,ALVIN M A,et al.Ultrasonic detection of delamination and material characterization of thermal barrier coatings[J].Journal of Thermal Spray Technology,2012,21(6):1184-1194. [24] BOUDA A B,LEBAILI S,BENCHAALA A.Grain size influence on ultrasonic velocities and attenuation[J].Ndt & E International,2003,36(1):1-5.
点击查看大图
计量
- 文章访问数: 1201
- HTML浏览量: 1
- PDF量: 1465
- 被引次数: 0