| Citation: | LIU Hua-wei, WANG Rong-qiao, HU Dian-yin. Effect of low cycle fatigue loading on the crack tip plastic zone of high cycle fatigue crack[J]. Journal of Aerospace Power, 2016, 31(10): 2339-2345. doi: 10.13224/j.cnki.jasp.2016.10.005
|
| [1] |
WANG Rongqiao,Cho C,NIE Jingxu.Combined fatigue life test and extrapolation of turbine disc mortise at elevated temperature[J].Journal of Engineering for Gas Turbines and Power,2005,127(4):863-868.
|
| [2] |
Hawkyard M,Powell E B,Hussey I,et al.Fatigue crack growth under the conjoint action of major and minor stress cycles[J].Fatigue & Fracture of Engineering Materials & Structures,1996,19(2/3):217-227.
|
| [3] |
Hall F R,Powell E B.Crack growth in IMI 829 at 550℃ under combined high and low cycle fatigue[J].Material at High Temperature,2002,19(1):1-8.
|
| [4] |
Zitounis V.Fatigue crack growth rates under variable amplitude load spectra containing tensile underloads[D].Bedfordshire,UK:Cranfield University,2003.
|
| [5] |
Newman J C,Jr.Prediction of fatigue crack growth under variable amplitude and spectrum loading using a crack closure model[C]//Design of Fatigue and Fracture Resistant Structures.Baltimore:American Society for Testing and Materials,1982:255-277.
|
| [6] |
Newman J C,Jr.A crack closure model for predicting fatigue crack growth under aircraft spectrum loading[C]//Methods and Models for Predicting Fatigue Crack Growth under Random Loading.Baltimore:American Society for Testing and Materials,1981:53-84.
|
| [7] |
Zhang W.Multi-resolution in-situ testing for fatigue crack growth mechanism investigation and model development[D].Potsdam,US:Clarkson University,2012.
|
| [8] |
ZHANG Wei,LIU Yongming.In situ SEM testing for crack closure investigation and virtual crack annealing model development[J].International Journal of Fatigue,2012,43(1):188-196.
|
| [9] |
侯静泳,蔡肇云,屠一鹤.TC-11钛合金高低周复合疲劳及损伤累积研究[J].航空动力学报,1992,7(2):135-138. HOU Jingyong,CAI Zhaoyun,TU Yihe.Research on high-low cycle complex fatigue and accumulative damage for Ti-alloy TC11[J].Journal of Aerospace Power,1992,7(2):135-138.(in Chinese)
|
| [10] |
许凤旌,聂景旭,赵长占.平板构件的高低周复合疲劳研究[J].航空动力学报,1992,7(2):121-124. XU Fengjing,NIE Jingxu,ZHAO Changzhan.A compound fatigue investigation of plate specimen under low-cycle load superposed on high cycle load[J].Journal of Aerospace Power,1992,7(2):121-124.(in Chinese)
|
| [11] |
许琦,潘升材.高低周复合载荷燕尾型榫连接微动疲劳的试验研究[J].航空动力学报,1997,12(4):407-409. XU Qi,PAN Shengcai.Fretting fatigue of dovetail joint under combined cyclic loading[J].Journal of Aerospace Power,1997,12(4):407-409.(in Chinese)
|
| [12] |
HU Dianyin,WANG Rongqiao.Combined fatigue experiments on full scale turbine components[J].Aircraft Engineering and Aerospace Technology,2013,85(1):4-9.
|
| [13] |
赵振华,陈伟.高低周复合载荷对TC11钛合金疲劳性能的影响[J].航空动力学报,2011,26(11):2468-2474. ZHAO Zhenhua,CHEN Wei.Effect of combined cycle load upon the fatigue performance of titanium alloy TC11[J].Journal of Aerospace Power,2011,26(11):2468-2474.(in Chinese)
|
| [14] |
赵振华,陈伟,吴铁鹰.高低周复合载荷对钛合金疲劳裂纹扩展性能的影响[J].机械科学与技术,2012,31(4):643-647. ZHAO Zhenhua,CHEN Wei,WU Tieying.The effect of combined cycle fatigue load on the fatigue crack propagation of titanium alloy[J].Mechanical Science and Technology for Aerospace Engineering,2012,31(4):643-647.(in Chinese)
|
| [15] |
黄金,杨邦成.Ⅰ型裂纹稳定扩展裂尖塑性区研究[J].交通科学与工程,2010,26(4):35-40. HUANG Jin,YANG Bangcheng.Research on plastic zone ofⅠ-type model crack extension stability[J].Journal of Transport Science and Engineering,2010,26(4):35-40.(in Chinese)
|
| [16] |
张丽,黄新跃,吴学仁,等.镍基高温合金GH4169小裂纹早期扩展的原位疲劳试验[J].航空动力学报,2014,29(4):901-906. ZHANG Li,HUANG Xinyue,WU Xueren,et al.In-situ experiment on early growth of small fatigue crack of nickel-based superalloy GH4169[J].Journal of Aerospace Power,2014,29(4):901-906.(in Chinese)
|
| [17] |
CHEN Jingjie,HUANG Yi,DONG Leilei,et al.A new method for cyclic crack-tip plastic zone size determination under cyclic tensile load[J].Engineering Fracture Mechanics,2014,126:141-154.
|
DownLoad: