Fatigue life prediction method based on the features of surface defects

doi: 10.13224/j.cnki.jasp.2019.01.011
  • Received Date: 2018-01-04
  • Publish Date: 2019-01-28
    Abstract
  • On the basis of fatigue data of specimen with surface defects, the size parameter of surface defects was proposed, and introduced into the Walker life equation to study the effect of size of surface defects. And the life prediction results of the equation were compared with the calculation results of life prediction method considering the stress gradient. The scatter bands of the results of two models were within ±3, indicating that the method is reliable. Then the equation was used in predicting the fatigue life of powder metallurgy turbine disk and obtaining the influence law of the surface defects with different sizes on the life of turbine disk. Its main engineering significance was that based on the stress characteristics of the dangerous position of turbine disk, the fatigue life with existence of the defect can be acquired. And even if the defects are not detected, it can ensure the safety in service period.

     

    • FullText(HTML)
  • loading
    • References(20)
  • [1]
    张丽娜,张麦仓,李晓,等.粉末高温合金中非金属夹杂问题的研究进展［J］.兵器材料科学与工程,2001,24(3):64-68.ZHANG Lina,ZHANG Maicang,LI Xiao,et al.Progress in study of nonmetallic inclusion in powder metallurgy (P/M) superalloys［J］.Ordnance Material Science and Engineering,2001,24(3):64-68.(in Chinese)
    [2]
    刘丽玉,陶春虎,刘昌奎,等.发动机粉末合金高压涡轮盘断裂的原因［J］.机械工程材料,2014,38(8):108-112.LIU Liyu,TAO Chunhu,LIU Changkui,et al.Fracture causes of powder metallurgy high pressure turbine disk of engine［J］.Materials for Mechanical Engineering,2014,38(8):108-112.(in Chinese)
    [3]
    刘新灵,陶春虎.FGH96粉末高温合金损伤行为与寿命预测［J］.失效分析与预防,2011,6(2):124-129.LIU Xinling,TAO Chunhu.Damage behavior and life prediction of FGH96 powder metallurgy superalloy［J］.Failure Analysis and Prevention,2011,6(2):124-129.(in Chinese)
    [4]
    GRISON J,REMY L.Fatigue failure probability in a powder metallurgy Ni-base superalloy［J］.Engineering Fracture Mechanics,1997,57(1):41-55.
    [5]
    SHAMBLEN C E,CHANG D R.Effect of inclusions on LCF life of HIP plus heat treated powder metal rené 95［J］.Metallurgical Transactions B,1985,16(4):775-784.
    [6]
    HURON E S,ROTH P G.The influence of inclusion on low cycle fatigue life in a P/M nickel-base disk superalloy［R］.Warrendale,Pennsylvania,USA:The Minerals,Metals and Materials Society,1996:359.
    [7]
    国为民,吴剑涛,张凤戈,等.FGH95镍基高温合金粉末中的夹杂及其对合金疲劳性能的影响［J］.粉末冶金工业,2000,10(3):23-28.GUO Weimin,WU Jiantao,ZHANG Fengge,et al.Inclusion in powder of nickle base superalloy FGH95 and the effect on LCF of the superalloy［J］.Powder Metallurgy Industry,2000,10(3):23-28.(in Chinese)
    [8]
    何承群,余泉茂,胡本芙.FGH95合金LCF断裂寿命与夹杂特征关系的研究［J］.金属学报,2001,37(3):247-252.HE Chengqun,YU Quanmao,HU benfu.Study of the relationship between the LCF life of FGH95 alloy and the inclusion characteristics［J］.Acta Metallurgica Sinica,2001,37(3):247-252.(in Chinese)
    [9]
    JABLONSKI D A.The effect of ceramic inclusions on the low cycle fatigue life of low carbon astroloy subjected to hot isostatic pressing［J］.Materials Science & Engineering,1981,48(2):189-198.
    [10]
    袁善虎.粉末冶金材料及结构的力学行为试验与数值模拟［D］.北京：北京航空航天大学，2014.YUAN Shanhu.Experiment and numerical modeling of the mechanical behaviors of a P/M superalloy and its structures［D］.Beijing:Beijing University of Aeronautics and Astronautics,2014.(in Chinese)
    [11]
    LANKFORD J.The growth of small fatigue cracks in 7075-T6 aluminum［J］.Fatigue & Fracture of Engineering Materials & Structures,1982,5(3):233-248.
    [12]
    ATZORI B,LAZZARIN P.Notch sensitivity and defect sensitivity under fatigue loading:two sides of the same medal［J］.International Journal of Fracture,2001,107(1):1-8.
    [13]
    El HADDAD M H,TOPPER T H,SMITH K N.Prediction of non propagating cracks［J］.Engineering Fracture Mechanics,1979,11(3):573-584.
    [14]
    左平.粉末高温合金小裂纹扩展规律研究［D］.北京:北京航空航天大学,2014.ZUO Ping.Study on the small crack characteristics in power metallurgy superalloy［D］.Beijing:Beijing University of Aeronautics and Astronautics,2014.(in Chinese)
    [15]
    MOREL F,MOREL A,NADOT Y.Comparison between defects and micro-notches in multiaxial fatigue:the size effect and the gradient effect［J］.International Journal of Fatigue,2009,31(2):263-275.
    [16]
    HERASYMCHUK O M,KONONUCHENKO O V,BONDARCHUK V I.Fatigue life calculation for titanium alloys considering the influence of microstructure and manufacturing defects［J］.International Journal of Fatigue,2015,81:257-264.
    [17]
    KUNZ L,LUK P,KONECˇN R R,et al.Casting defects and high temperature fatigue life of IN 713LC superalloy［J］.International Journal of Fatigue,2012,41:47-51.
    [18]
    VINCENT M,NADOT-MARTIN C,NADOT Y,et al.Fatigue from defect under multiaxial loading:defect stress gradient (DSG) approach using ellipsoidal equivalent inclusion method［J］.International Journal of Fatigue,2014,59:176-187.
    [19]
    王延荣,李宏新,袁善虎,等.考虑应力梯度的缺口疲劳寿命预测方法［J］.航空动力学报,2013,28(6):1208-1214.WANG Yanrong,LI Hongxin,YUAN Shanhu,et al.Method for notched fatigue life prediction with stress gradient［J］.Journal of Aerospace Power,2013,28(6):1208-1214.(in Chinese)
    [20]
    陈光.一起奇特的高压涡轮非包容故障:左发甩出的涡轮盘断块打入右发尾喷管中［J］.航空发动机,2009,35(1):60-62.
    • Relative Articles
    • Supplements(0)
    • Cited By
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索
    Get Citation
    PDF(767.0KB)
    XML

    Article Metrics

    Article views (1077) PDF downloads(836) Cited by()
    Proportional views
    Related

    Copyright © 《Journal of Aerospace Power》 All Rights Reserved.

    Supported by: Beijing Renhe Information Technology Co., Ltd.  

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return