DZ125光滑试样与小孔构件低循环/保载疲劳寿命建模

周天朋; 杨晓光; 石多奇; 候贵仓; 丛佩红

DZ125光滑试样与小孔构件低循环/保载疲劳寿命建模

1.
北京航空航天大学能源与动力工程学院, 北京 100083
2.
沈阳发动机设计研究所, 沈阳 110015

计量
- 文章访问数: 1654
- HTML浏览量: 217
- PDF量: 428
- 被引次数: 0
出版历程
- 收稿日期: 2007-01-19
- 修回日期: 2007-04-04
- 刊出日期: 2008-02-28

Modeling of low-cycle and creep fatigue life for DZ125 smooth specimens and small-hole components

1.
School of Jet Propulsion, Beijing University of Aeronautics and Astronautics, Beijing 100083, China
2.
Shenyang Aeroengine Research Institute, Shenyang 110015, China

摘要

摘要: 依据定向结晶合金DZ125光滑试样的低循环/保载疲劳试验寿命数据,提出一种预测定向结晶合金低循环/保载疲劳寿命的模型.此寿命模型可以同时考虑材料的晶向、平均应力、应变范围、应变比、最大应力对寿命的影响.接着研究DZ125合金光滑试样低循环/保载疲劳寿命与小孔构件低循环/保载疲劳寿命的关系,提出一种从光滑试样低循环/保载疲劳寿命数据预测小孔构件低循环/保载疲劳寿命的方法.应用本文提出的寿命模型,预测DZ125带小孔构件的低循环/保载疲劳寿命,并将预测寿命与小孔构件试验寿命对比,误差在2倍分散带左右.
- 航空、航天推进系统 /
- DZ125 /
- 定向结晶 /
- 疲劳 /
- 蠕变 /
- 寿命
Abstract: Alow cycle fatigue and creep life prediction model of DZ125 was established according to the fatigue and creep experimental life data of directionally solidified DZ125 smooth specimens.This model also considered the influences of crystal direction,average stress,strain range,strain ratio and the greatest stress on the life.Then,the relationship of low-cycle fatigue and creep life between smooth specimens and small-hole components was discussed,and a method was developed to predict the low-cycle fatigue and creep life of DZ125 small-hole components from that of directionally solidified DZ125 smooth specimens.The results show that,this model can predict comparatively the low cycle fatigue and creep life,indicating that the error of life prediction results are about two times of dispersion band.
- aerospace propulsion system /
- DZ125 /
- directionally solidified /
- fatigue /
- creep /
- life model.

HTML

参考文献(12)

[1]	苏清友,孔瑞莲.航空涡喷/涡扇发动机主要零部件定寿指南[M].北京:航空工业出版社,2004.
[2]	张晓兵,李其连.激光加工小孔工艺及其孔壁再铸层对DZ22高温合金疲劳性能的影响[J].新技术新工艺,1995,(2):20-22.ZHANG Xiaobin,LI Qilian.Laser drilling of small hole and the influence of recasting layer on fatigue performance of DZ22 superalloy[J].New Technology & New Process,1995,(2):20-22.
[3]	汪浩.缺口曲率半径对30CrMnSiA钢疲劳萌生寿命的影响[J].机械制造与自动化,2003,(3):29-35.WANG Hao.The effect of notch curvature radius on fatigue life of 30CrMnSiA steel[J].Machine Building & Automation,2003,(3):29-35.
[4]	刘灵灵,王建国.GH4169缺口件多轴加载下应力应变场的有限元分析[J].物理测试,2005,23(3):11-13.LIU Lingling,WANG Jianguo.Stress-strain field FEM analysis for GH4169 notched specimens under multiaxial loading[J].Physics Examination and Testing,2005,23(3):11-13.
[5]	罗毅,黄培彦,周希平.缺口件疲劳裂纹形成特性研究[J].华南理工大学学报,2006,28(6):34-38.LUO Yi,HUANG Peiyan,ZHOU Xiping.Research on fatigue crack formation of notched specimen[J].Journal of South China University of Technology,2006,28(6):34-38.
[6]	Barter S,Molent L,Goldsmith N,et al.An experimental evaluation of fatigue crack growth[J].Engineering Failure Analysis,2005,(12):99-128.
[7]	Meraha N,Bui-Quoc T,Bernard M.Creep-fatigue crack growth in notched SS-304 plates at 600℃[J].Engineering Fracture Mechanics,1999,(63):39-55.
[8]	Lukas P,Preclik P,Cadek J.Notch effects on creep behaviour of CMSX-4 superalloy single crystals[J].Materials Science and Engineering,2001,A298:84-89.
[9]	Smith R N,Watson P,Topper T H.A stress-strain function for the fatigue of metals[J].Journal of Materials,JMLSA,1970,5:767-778.
[10]	张锦,张乃恭.新型复合材料力学机理及其应用[M].北京:北京航空航天大学出版社,1993:40-53.
[11]	北京航空材料研究所.航空发动机设计用材料数据活页手册(DZ125)[M].国防工业出版社,2000:17-18.
[12]	ZHOU Tianpeng,YANG Xiaoguang,SHI Duoqi.Visoplastic deformation simulation for directionally solidified super alloy DZ125[C]//Proceedings of the 1st International Symposium on Jet propulsion and Power Engineering.Kunming China:School of Jet Propulsion,Beijing University of Aeronautics and Astronautics,2006,(1):195-200.